Advantages
Water-based, non-toxic, and environment-friendly green product High-build elastomeric, micro-porous coating Excellent resistance to carbon dioxide, air-borne, and water-borne chlorides Outstanding crack-bridging properties and weathering resistance Protective and decorative coating that allows the structure to breathe Application Bridge abutments External concrete surfaces of storage tanks and masonry surfaces Multistoried buildings and villas High external tough UV-resistant coating such as on pipe protection enamel and concrete cladding Subways
Application
Bridge abutments
External concrete surfaces of storage tanks and masonry surfaces
Multistoried buildings and villas
High-external tough UV-resistant coating such as on pipe protection enamel and concrete cladding Subway
Application Methodology
Remove dust, flakes, oil, grease, or other loose foreign particles using sandblasting, an iron brush, or compressed air. Remove oil, grease, chemical contaminants, and extraneous matter. Ensure that the substrate is sound, clean, and free from dust and all loose or flaking material. Fill all holes and deep cracks with a suitable filler. Ensure that no trace of mold or algae remains and that the area is treated with a suitable antifungicide or bleach solution. For new cementitious substrates, ensure that the substrate is fully cured for at least 14 days. Stir drums thoroughly for uniformity. For best results, use a variable speed drill mixer with a spiral-type blade at the bottom of the stirrer rod at a speed of 400-600 rpm. Dilute CLI Coat AWB by adding 10% clean water by volume and prime old, absorbent, and weathered surfaces. On non-porous surfaces, apply CLI Coat AWB undiluted. Prime all metal substrates with CLI Prime Zn 40. Apply CLI Coat AWB evenly at temperatures between 3°C and 30°C with a roller, brush, or airless spray. Use a two-coat system on dark, absorbent, and heavily textured surfaces and when full carbonation protection is required. Porous, rough, and irregular surfaces will reduce coverage rates.
Characteristics
| # | Characteristic | Value |
|---|---|---|
| 1 | pH | 9-11 |
| 2 | Thinning Agent | Water |
| 3 | CO2 Resistance Equivalent Air Layer | 123m @ 160 μ W thickness |
| 4 | CO2 Resistance Equivalent Air Layer | 123m @ 160 μ W thickness |
| 5 | Water Vapor Permeability (24 hrs) | 0.02 mg |
| 6 | Resistance to Weather | Very Good |
| 7 | Surface Structure | Smooth |
| 8 | Binders | Pure Acrylate |
| 9 | Density | 1.35 g/cm³ approx |
| 10 | Water Absorption (DIN 52617) | w < 0.2 kg/m²·hr |
| 11 | CO2 Diffusion Coefficient | 6.4 x 10⁵ |
Storage and Shelf Life
Store in a cool, dry place at temperatures between 5°C and 30°C, under shade, away from heat. The shelf life of the product is 1 year in original unopened sealed condition.