Key Features
- Solvent-free and clear
- Moisture-curing with long-term elasticity
- Excellent adhesion to rubber granulates
- High tensile strength and durability
Recommended Uses
Carbolink XP 14 Water Clear is used for:
Creating base layers for running track systems
Base coats for playgrounds and tennis courts
Application GuidelinesSurface Preparation:
• Ensure surfaces are dry and free of dust, loose particles, and other contaminants.
• Clean surfaces thoroughly before application.
• Prime surfaces with XP 13 Primer using an airless sprayer and brush. The base layer should be constructed while the XP 13 Primer is still sticky (wet-on-wet application). Curing occurs at ambient temperature through solvent evaporation and reaction with atmospheric moisture.
• Mix XP 14 Water Clear with recycled rubber using a low-revolution mixer (300-600 rpm) for 1-2 minutes until homogeneous.
• Pour the mixture onto the surface and spread to a thickness of 11 to 12mm using a suitable paving machine or hand straightedge and flat trowel. Roll the surface with a metallic cylinder to remove minor irregularities.
• Ensure the temperature does not fall below ten °C during curing.
• Curing time depends on temperature and humidity, taking approximately 48-72 hours.
Consumption
• Mixture: 1.32 kg XP 14 Water Clear with 6 kg recycled rubber (granulometry 0.5-2.5mm)
• Ratio: 18.3% XP 14 Water Clear to 81.7% recycled rubber
Technical Specifications
| # | Characteristic | Value |
|---|---|---|
| 1 | Type | One-component polyurethane |
| 2 | Appearance | Liquid |
| 3 | Color | Transparent |
| 4 | Viscosity | 4,000 – 8,000 mPa.s at 25°C |
| 5 | Density | 1.08 – 1.18 Kg/L at 25°C |
| 6 | Application Temperature | 10 – 40°C |