FEATURES

Hard wearing
Resistant to a wide range of chemicals and liquids
Suitable for use in food and drinks production environments
Seamless - easily cleaned to maintain high standards of hygiene

STANDARD COLORS

Available to any standard RAL Card upon request

SURFACE PREPARATION

All substrates must be clean and free from dust and loose particles. All traces of contaminants, such as oils, fats, greases, paint residues, chemicals, algae and other barriers to adhesion should be removed. Good surface preparation is vital to ensure the successful application and performance of IF 10 C.

As IF 10 C is used on previously applied polyurethane floors appropriate surface preparation techniques will depend on the condition of the floor. If the floor is less than 48 hours old the IF 10 C can be applied directly after any dust and contamination is removed. Older floors will require surface grinding or abrasion with a coarse nylon pad in combination with a strong alkali detergent.

PRIMING

Pour the contents of Part A and Part B into a small mixing bucket and mix using a small helical mixing paddle and electric drill for 30 seconds or until uniform. The contents of Part C and Part D should then be introduced into the mixed resin and mix together for further 2 minutes to create one homogenous mix.

APPLICATION

The mixed material should be applied without delay to the prepared substrate using a brush, roller or rubber squeegee, depending on thickness and finish required. Roll in a scatter of Fine Aggregate to give a slip resistant texture if required.
If used to reduce the texture of an existing floor surface, care should be taken to ensure the application is uniform and leaves the appropriate finish intended. For repairs pour into cracks, topping up as necessary, or apply with a spatula for cracks up to 5 mm, isolated areas up to 10 mm wide.

For larger cracks / repairs mix in up to half volume of Fine Aggregate. Once cured overcoat with an application of neat IF 10 C.

LIMITATIONS

Only apply IF 10 C at temperatures above 5°C and where the atmospheric relative humidity (RH) is 90% or below. Do not apply when atmospheric condensation may occur before the IF 10 C is fully cured. The working life is approx. 8 minutes. Multiple units may be mixed but do not mix more material than can be applied within the 8 minutes working time. Attempting to use the IF 10 C more than 10 minutes after mixing will result in a patchy, variable finish.

CLEANING

IF 10 C can be removed from tools and equipment by using CLI Eco Sol 205 immediately after use. Any hardened material will need to be removed mechanically.

PROPERTIES

The values shown are typical of results obtained in the laboratory at 27 ± 1ºC. Actual performance values obtained on site may vary from those quoted.

PHYSICAL PROPERTIES